NEWS ANALYSIS


Today, the likes of Infineon and Cree are busy developing SiC devices based on 4H SiC crystalline materials. This polymorph is grown via PVT as a single crystal and then sliced to produce relatively defect-free wafers, up to 6-inches in diameter. However, the growth process is slow and energy-intensive, yielding very pricey substrates.


But a second polymorph could provide an alternative. In theory, layers of 3C-SiC could be grown epitaxially on silicon wafers as this polymorph has a cubic crystal structure just like silicon. But while the resulting wafer could be produced much more cheaply than a 4H-SiC wafer, lattice mismatches and differences in thermal expansion coefficients between the 3C-SiC layers and silicon seed wafer induce in-plane stresses that cause wafer bowing. Device performance plummets and so manufacturers have stuck with the costly 4H-SiC wafers.


However, Ward, and colleagues, have developed a novel, low pressure CVD 3C-SiC growth process, that they claim bypasses these problems. Prior to SiC growth, a mask is placed over the silicon wafer to define structures in the scribe lines of the wafer. The team then deposits a 1.5 µm-thick layer of heavily doped, dislocated material onto the silicon seed wafer. This helps to relieve stresses from lattice mismatches that lead to wafer bowing, and also allows vertical conduction through the interface.


“This layer is doped with dopants from the silicon wafer and nitrogen, allowing us to conduct through the silicon carbide- silicon heterojunction,” says Ward. “So we can conduct from the top to the back of the wafer and have built devices where you cannot see additional resistance at the interface. This makes us very competitive with GaN-on-silicon, which can’t conduct vertically.”


In the same run, monocrystalline SiC is then grown in the die areas between the scribe lines, with polycrystalline SiC forming in the scribe lines. As Ward says: “We are effectively interfering with the epi-process and producing polycrystalline SiC in the scribe lines while growing single crystalline epilayers where we want to build the device.”


Crucially, the resulting mesh of polycrystalline SiC helps to relieve the thermal expansion differential stresses across the wafer that also lead to bowing.


“Instead of trying to fabricate a 100 mm wafer, in terms of stress we are effectively making a 5 mm die,” he adds. “This makes our process very scalable and essentially independent of wafer diameter.”


Indeed, as Ward highlights, his company is only limited to 100 mm wafer sizes at the moment due to the industry’s shortage of higher temperature, large wafer diameter epi- reactors.“Silicon reactors typically run at 1000 °C, but we need a reactor that has been designed to reach 1370 °C and the only ones that exist have been built for [100 mm] 4H SiC wafers,” he explains. “So there aren’t so many of these reactors right now, but we know where they are and who they belong to, and we’ve worked with most of these [organisations].”


Ward is also adamant the process is scalable to mass production, stating: “ I have spent more decades than I would care to working with silicon, and having spent a lifetime


The Anvil Semiconductor team has been working with researchers at the University of South Florida to hone SiC device development and reactor technology


January / February 2014 www.compoundsemiconductor.net 17 “


We hope to stay as a niche product manufacturer but we


see a very clear value chain from Schottky diodes to MOSFETs and probably to driver circuits as well.


manufacturing silicon devices, I see no reason why this shouldn’t scale.”


In the meantime, the Anvil team is busy building prototypes. A standard Schottky diode, similar to 4H-SiC versions but cheaper, is scheduled for release in 2014. And the company is also running a parallel MOSFET program, which could see prototype devices being released six months after the first Schottky diodes.





Ward won’t talk about performance figures yet, only to say his team is pushing for very low on-resistance devices and is focusing on producing 650 V Schottky diodes and MOSFETs. As he explains, using 3C-SiC on silicon, his team can fabricate a very cost competitive 650 V device.


“Once we prove these 3C-SiC devices are a go-er we will start licensing commodity products,” he adds. “We hope to stay as a niche product manufacturer but we see a very clear value chain from Schottky diodes to MOSFETs and probably to driver circuits as well.”


© 2014 Angel Business Communications. Permission required.


Page 1  |  Page 2  |  Page 3  |  Page 4  |  Page 5  |  Page 6  |  Page 7  |  Page 8  |  Page 9  |  Page 10  |  Page 11  |  Page 12  |  Page 13  |  Page 14  |  Page 15  |  Page 16  |  Page 17  |  Page 18  |  Page 19  |  Page 20  |  Page 21  |  Page 22  |  Page 23  |  Page 24  |  Page 25  |  Page 26  |  Page 27  |  Page 28  |  Page 29  |  Page 30  |  Page 31  |  Page 32  |  Page 33  |  Page 34  |  Page 35  |  Page 36  |  Page 37  |  Page 38  |  Page 39  |  Page 40  |  Page 41  |  Page 42  |  Page 43  |  Page 44  |  Page 45  |  Page 46  |  Page 47  |  Page 48  |  Page 49  |  Page 50  |  Page 51  |  Page 52  |  Page 53  |  Page 54  |  Page 55  |  Page 56  |  Page 57  |  Page 58  |  Page 59  |  Page 60  |  Page 61  |  Page 62  |  Page 63  |  Page 64  |  Page 65  |  Page 66  |  Page 67  |  Page 68  |  Page 69  |  Page 70  |  Page 71  |  Page 72  |  Page 73  |  Page 74  |  Page 75  |  Page 76  |  Page 77  |  Page 78  |  Page 79  |  Page 80  |  Page 81  |  Page 82  |  Page 83  |  Page 84  |  Page 85  |  Page 86  |  Page 87  |  Page 88  |  Page 89  |  Page 90  |  Page 91  |  Page 92  |  Page 93  |  Page 94  |  Page 95  |  Page 96  |  Page 97  |  Page 98  |  Page 99  |  Page 100  |  Page 101  |  Page 102  |  Page 103  |  Page 104  |  Page 105  |  Page 106  |  Page 107  |  Page 108  |  Page 109  |  Page 110  |  Page 111  |  Page 112  |  Page 113  |  Page 114  |  Page 115  |  Page 116  |  Page 117  |  Page 118  |  Page 119  |  Page 120  |  Page 121  |  Page 122  |  Page 123  |  Page 124  |  Page 125  |  Page 126  |  Page 127  |  Page 128  |  Page 129  |  Page 130  |  Page 131  |  Page 132  |  Page 133  |  Page 134  |  Page 135  |  Page 136  |  Page 137  |  Page 138  |  Page 139  |  Page 140  |  Page 141  |  Page 142  |  Page 143  |  Page 144  |  Page 145  |  Page 146  |  Page 147  |  Page 148  |  Page 149  |  Page 150  |  Page 151  |  Page 152  |  Page 153  |  Page 154  |  Page 155  |  Page 156  |  Page 157  |  Page 158  |  Page 159  |  Page 160  |  Page 161  |  Page 162  |  Page 163  |  Page 164  |  Page 165  |  Page 166  |  Page 167  |  Page 168  |  Page 169