research review Improving polar InN surfaces to enable
the fabrication of p-njunctions Using a simple nitridation process,it is now possible to grow up to 25 nm-thick polar InN films with the surface Fermi level close to the valence band maximum
A FINNISH-RUSSIAN-SWEDISH collaboration is claiming that it has used ammonia nitridation to produce the first polar InN with the surface Fermi level near the valence-band maximum.
In the past, the growth of polar InN films has been hindered due to metallic indium clusters, formed readily during growth, and unintentional n-type conductivity of nominally undoped films. These include surface electron-accumulation layers via the Fermi level pinning into the conduction band.
These issues have hampered, for example, the realisation of p-type InN layers. This makes it difficult to grow p-n junctions in InN layers, which are needed in a wide range of devices.
A team from the Institute of Solid State Theory, Friedrich Schiller University and the European Theoretical Spectroscopy Facility, all based in Germany, using ab initio calculations, recently predicted the Fermi level position for InN.
Furthermore, researchers at Ritsumeikan University in Japan and Seoul National University, Korea, have shown that the plasma nitridations during growth stop the transformation of even large indium clusters into two-dimensional InN islands, improving InN quality.
Now researchers, led by a team at the University of Turku in Finland, have shown that high electron concentrations can be avoided, which is promising for making p-type InN films.
They initially grew InN films on silicon (111) and GaN (0001) substrates by the nitridation of the indium-covered semiconductor surfaces with ammonia (NH3
) or cracked N2 gas.
Following this treatment, the scientists found it was possible to grow up to 25 nm thick polar InN films with the surface Fermi level close to the valence band maximum. In other words, they avoided the presence of electron accumulation layers.
(a) STM image showing two-dimensional nature of InN (000)/Si (111) sample (~ 800 nm x 800 nm) (b) STM image showing two-dimensional nature of InN (000)/GaN (0001) sample (~450nm x 450nm) (c) Synchrotron-radiation In 4d core-level photoelectron spectra show that the nitridation transforms metallic indium to InN (d) Analysis of current-voltage curves,measured by STS from well-defined surface areas,reveal that the surface Fermi level locates close to the valence-band maximum
The substrate temperature during the nitridation was found to be one of the most crucial parameters in the formation of InN (0001) films with the Fermi level near the valence-band maximum.
Indium was evaporated from a heated tantalum envelope onto the substrates, which were kept at room temperature before nitridations. The NH3 about 5 x 10-5 nitridation.
mbar during the
Temperature of indium-covered silicon (111) substrates was 400 - 450 °C during the nitridation, and the temperature for
indium-covered GaN (0001) pieces was 530 - 580 °C, just below the decomposition temperature of InN.
The silicon (111) substrates were flash heated at about 1200 °C. Scanning tunnelling microscopy indicates a smooth, well-defined (7x7)-reconstructed surface.
pressure was
To clean HVPE-grown n-type GaN (0001) substrate pieces, they were heated to around 600 °C in the NH3
get a sharp (1 x 1) diffraction.
J. Dahl et al Phys. Review B 86 245304 (2012)
January / February 2013
www.compoundsemiconductor.net 75
atmosphere to
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46 |
Page 47 |
Page 48 |
Page 49 |
Page 50 |
Page 51 |
Page 52 |
Page 53 |
Page 54 |
Page 55 |
Page 56 |
Page 57 |
Page 58 |
Page 59 |
Page 60 |
Page 61 |
Page 62 |
Page 63 |
Page 64 |
Page 65 |
Page 66 |
Page 67 |
Page 68 |
Page 69 |
Page 70 |
Page 71 |
Page 72 |
Page 73 |
Page 74 |
Page 75 |
Page 76 |
Page 77 |
Page 78 |
Page 79 |
Page 80 |
Page 81 |
Page 82 |
Page 83 |
Page 84 |
Page 85 |
Page 86 |
Page 87 |
Page 88 |
Page 89 |
Page 90 |
Page 91 |
Page 92 |
Page 93 |
Page 94 |
Page 95 |
Page 96 |
Page 97 |
Page 98 |
Page 99 |
Page 100 |
Page 101 |
Page 102 |
Page 103 |
Page 104 |
Page 105 |
Page 106 |
Page 107 |
Page 108 |
Page 109 |
Page 110 |
Page 111 |
Page 112 |
Page 113 |
Page 114 |
Page 115 |
Page 116 |
Page 117 |
Page 118 |
Page 119 |
Page 120 |
Page 121 |
Page 122 |
Page 123 |
Page 124 |
Page 125 |
Page 126 |
Page 127 |
Page 128 |
Page 129 |
Page 130 |
Page 131 |
Page 132 |
Page 133 |
Page 134 |
Page 135 |
Page 136 |
Page 137 |
Page 138 |
Page 139 |
Page 140 |
Page 141 |
Page 142 |
Page 143 |
Page 144 |
Page 145 |
Page 146 |
Page 147 |
Page 148 |
Page 149 |
Page 150 |
Page 151 |
Page 152 |
Page 153 |
Page 154 |
Page 155 |
Page 156 |
Page 157 |
Page 158 |
Page 159 |
Page 160 |
Page 161 |
Page 162 |
Page 163 |
Page 164 |
Page 165 |
Page 166 |
Page 167 |
Page 168 |
Page 169 |
Page 170 |
Page 171 |
Page 172 |
Page 173 |
Page 174 |
Page 175 |
Page 176 |
Page 177 |
Page 178 |
Page 179 |
Page 180 |
Page 181 |
Page 182 |
Page 183 |
Page 184 |
Page 185 |
Page 186 |
Page 187 |
Page 188 |
Page 189 |
Page 190 |
Page 191 |
Page 192 |
Page 193 |
Page 194 |
Page 195 |
Page 196 |
Page 197 |
Page 198 |
Page 199 |
Page 200 |
Page 201 |
Page 202 |
Page 203 |
Page 204 |
Page 205 |
Page 206 |
Page 207 |
Page 208 |
Page 209 |
Page 210 |
Page 211 |
Page 212 |
Page 213 |
Page 214 |
Page 215 |
Page 216 |
Page 217 |
Page 218 |
Page 219 |
Page 220 |
Page 221 |
Page 222 |
Page 223 |
Page 224 |
Page 225 |
Page 226 |
Page 227 |
Page 228 |
Page 229 |
Page 230 |
Page 231 |
Page 232 |
Page 233