RESEARCH REVIEW


Refining periodically orientated GaN Non-linear optics could benefit from alternating layers of N-polar and Ga-polar GaN.


Researchers from the US Naval Research Laboratory are claiming to have developed a superior approach to making a structure with selectively switched GaN polarity.


“[Our work] is a breakthrough,” says team-member Jennifer Hite. She explains that the team have demonstrated a simple method for forming a thin sapphire-like layer on Ga-polar GaN. This process holds the key to polarity changes from Ga-polar to N-polar material.


Kite believes that this simple method is preferable to the previous best approach: That required a magnesium-based layer for inversion of GaN, and had unwanted side effects, such as uncontrolled formation of inversion domains and faceted interfaces.


“The biggest application space for our work is in non-linear optics, basically using the alternating polarity for frequency conversion through quasi- phase matching.” For a semiconductor structure to realise quasi-phase matching, its crystal orientation must be periodically altered to produce a large second order non-linearity.


Quasi-phase matching in GaN was reported in 2003 by a team from Bell Laboratories, New Jersey. However, in that case the researchers employed GaN


Transmission electron microscopy reveals the damage to the annealed Al2


O3 interface with GaN


heteroepitaxial thin films on sapphire, which add strain and limit the thickness of the structure. A thickness of a millimetre or more is needed, which accounts for the interest in GaN-on-GaN structures for high-power, non-linear optics.


The starting point for forming such


structures is a 2 μm-thick film of c-plane GaN deposited on a-plane sapphire by MOCVD. Following chemical cleaning, this epiwafer is placed in an ALD tool and a 15 nm-thick film deposited. After patterning 16 µm-wide stripes with a positive photo-resist and photolithography technique, etching in hydrofluoric acid removes Al2


O3 designated regions of the wafer. from near the


on Ga-polar GaN, before the wafer is loaded into an MOCVD chamber. Annealing in an ammonia atmosphere at 1100 °C for 40 minutes converts amorphous Al2


O3 O3 to a crystalline form,


before a GaN buffer is deposited at 670 °C, followed by GaN growth at 1100 °C.


Using two growth steps and an intermediate clean is the only way to make periodically orientated semiconductor structures. That may mean it’s viewed as a complex process, but this not a barrier to volume manufacturing, insists Kite: “Silicon technologies require multiple tools and growth steps – Intel has actually


incorporated ALD to deposit high-κ dielectrics.”


Researchers confirm the presence of N-polar and Ga-polar regions by etching samples for up to 40 minutes in potassium hydroxide. N-polar material is far more chemically reactive than its Ga-polar cousin, with etching creating hexagonal faceting, while the Ga-polar material maintains a smooth surface.


Studies of initial structures identified N-polar regions with ‘lips’ of material along the border and ‘troughs’ in the middle. Lowering the V/III ratio enables a coalesced, more uniform N-polar structure. However, further optimisation is needed, because there are Ga-polar inclusions in the N-polar areas.


Scrutinising structures with a transmission electron microscope reveals that all the GaN is c-orientated. The interface between the Al2


O3


sharp, but the bottom 10 nm of Al2 damaged, due to annealing.


and the upper GaN is O3


is


Plans for the future begin with reducing Ga- polar inclusions by optimising the N-polar initiation on the ALD layer. “The following step will be to grow thick structures by HVPE, and then test the material for quasi-phase matching,” says Hite.


J. Hite et. al.


Periodically orientated GaN is formed with a process involving atomic layer deposition (ALD) of amorphous Al2


O3 , which takes on a more crystalline form after annealing March 2014 www.compoundsemiconductor.net 77 Appl. Phys. Express 7 025502 (2014)


Stripping the photoresist leaves stripes of Al2


Page 1  |  Page 2  |  Page 3  |  Page 4  |  Page 5  |  Page 6  |  Page 7  |  Page 8  |  Page 9  |  Page 10  |  Page 11  |  Page 12  |  Page 13  |  Page 14  |  Page 15  |  Page 16  |  Page 17  |  Page 18  |  Page 19  |  Page 20  |  Page 21  |  Page 22  |  Page 23  |  Page 24  |  Page 25  |  Page 26  |  Page 27  |  Page 28  |  Page 29  |  Page 30  |  Page 31  |  Page 32  |  Page 33  |  Page 34  |  Page 35  |  Page 36  |  Page 37  |  Page 38  |  Page 39  |  Page 40  |  Page 41  |  Page 42  |  Page 43  |  Page 44  |  Page 45  |  Page 46  |  Page 47  |  Page 48  |  Page 49  |  Page 50  |  Page 51  |  Page 52  |  Page 53  |  Page 54  |  Page 55  |  Page 56  |  Page 57  |  Page 58  |  Page 59  |  Page 60  |  Page 61  |  Page 62  |  Page 63  |  Page 64  |  Page 65  |  Page 66  |  Page 67  |  Page 68  |  Page 69  |  Page 70  |  Page 71  |  Page 72  |  Page 73  |  Page 74  |  Page 75  |  Page 76  |  Page 77  |  Page 78  |  Page 79  |  Page 80  |  Page 81  |  Page 82  |  Page 83  |  Page 84  |  Page 85  |  Page 86  |  Page 87  |  Page 88  |  Page 89  |  Page 90  |  Page 91  |  Page 92  |  Page 93  |  Page 94  |  Page 95  |  Page 96  |  Page 97  |  Page 98  |  Page 99  |  Page 100  |  Page 101  |  Page 102  |  Page 103  |  Page 104  |  Page 105  |  Page 106  |  Page 107  |  Page 108  |  Page 109  |  Page 110  |  Page 111  |  Page 112  |  Page 113  |  Page 114  |  Page 115  |  Page 116  |  Page 117  |  Page 118  |  Page 119  |  Page 120  |  Page 121  |  Page 122  |  Page 123  |  Page 124  |  Page 125  |  Page 126  |  Page 127  |  Page 128  |  Page 129  |  Page 130  |  Page 131  |  Page 132  |  Page 133  |  Page 134  |  Page 135  |  Page 136  |  Page 137  |  Page 138  |  Page 139  |  Page 140  |  Page 141  |  Page 142  |  Page 143  |  Page 144  |  Page 145  |  Page 146  |  Page 147  |  Page 148  |  Page 149  |  Page 150  |  Page 151  |  Page 152  |  Page 153  |  Page 154  |  Page 155  |  Page 156  |  Page 157  |  Page 158  |  Page 159  |  Page 160  |  Page 161  |  Page 162  |  Page 163  |  Page 164