GaP-on-silicon Scrutinising samples with several microscopes reveals the presence of anti-phase boundaries in GaP that jump from one atomic plane to another.
FOR MANY YEARS, engineers have dreamed of the possibilities that would result from monolithic integration of III-V transistors and lasers on large, low-cost silicon substrates. And GaP has been marked out as a compound with a big role to play, thanks to its very favourable lattice constant – but little is known about the boundaries between device- degrading anti-phase domains that can form in this binary when it is deposited on silicon.
To address this shortcoming, researchers from the Philipps University Marburg and Jülich Research Centre have carried out a theoretical and experimental study into the nature of the anti-phase boundaries found in GaN grown on silicon. This team was surprised with what they found: “Theory predicted something different from what was experimentally observed,” explains team member Kerstin Volz from Philipps University Marburg. The anti- phase boundaries were not atomically abrupt, as expected, but have a finite thickness, due to random jumps between atomic planes.
One key finding by the team is that the jumping between planes can lead to a charge distribution that is macroscopically neutral along some planes, but leads to local charging along others.
“If there are free charges, even if macroscopically neutral, these charges can still have an impact on the functionality of devices that rely on charged carrier transport,” explains Volz. “Knowing the structure of these defects and correlating the structure to the growth conditions will allow us to control the charge distribution in these layers.”
Samples for the team’s study were formed by using MOCVD to deposit a GaP layer on a silicon (100) substrate with an intentional miscut of 0.1° in the [110] direction.
One example of this is that despite having a lower mean atomic number than GaAs, GaNAs produces a higher intensity.
Viewing along the [110] direction, Volz and his co-workers acquired images showing an anti-phase boundary with a thickness of one atomic layer in the GaP film. They explained this by arguing that the anti-phase boundary is not fixed on a {110}-plane, but jumps from one {110}-plane in the viewing direction to another.
High angular dark-field imaging on GaP grown on silicon reveals the nature of anti-phase domains, which can lead to device-degrading free charges
“Growth conditions are chosen in a way that no twins or stacking faults occur, and only a minimum of anti-phase domains remain,” reveals Volz. To realise this, the deposition process includes a pulsed nucleation step at 450 °C and continuous overgrowth at 675 °C.
High-angle, angular dark-field (HAARF) images of the electron-transparent samples that were prepared from the epiwafers were obtained with three different scanning tunnelling electron microscopes: a JOEL ARM 200F, a JEOL 2200 FS, and an FEI Titan 80-300. Spherical aberrations of specific lenses were corrected to realise the high level of resolution.
To complement these measurements, the team calculated HAARF-intensities using commercial software.
According to Volz, it is essential to carry out these simulations: “The often-used assumption that the HAADF intensity is proportional to the square of the atomic number is just a rough approximation. In reality, the contrast is more complex, and depends on imaging conditions, as well as sample properties, such as strain.”
To confirm the presence of these jumps, the team looked at cross-section samples in a <110> projection. This revealed that the anti-phase boundary does not run straight along a charge-neutral [110]-plane, but is facetted on higher indexed planes.
Volz believes that these jumps may be driven by temperature, so they could be supressed by lowering the deposition temperature. “However, a certain temperature is needed for decomposition of the precursors, which makes the jumps unavoidable.”
The jumps are not necessarily bad news, because they can provide a mechanism for self-annihilation of the anti-phase domains. The German team have done this, producing a GaP-on-silicon (001) template that is free from anti-phase domains after 50 nm of deposition of the binary compound.
Goals for the team are to now perform calculations to estimate the energy of the jumps, and to carry out additional HAADF measurements to determine the three- dimensional nature of the anti-phase domains.
A. Beyer et. al. Appl. Phys. Lett. 103 032107 (2013) August / September 2013
www.compoundsemiconductor.net 61
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46 |
Page 47 |
Page 48 |
Page 49 |
Page 50 |
Page 51 |
Page 52 |
Page 53 |
Page 54 |
Page 55 |
Page 56 |
Page 57 |
Page 58 |
Page 59 |
Page 60 |
Page 61 |
Page 62 |
Page 63 |
Page 64 |
Page 65 |
Page 66 |
Page 67 |
Page 68 |
Page 69 |
Page 70 |
Page 71 |
Page 72 |
Page 73 |
Page 74 |
Page 75 |
Page 76 |
Page 77 |
Page 78 |
Page 79 |
Page 80 |
Page 81 |
Page 82 |
Page 83 |
Page 84 |
Page 85 |
Page 86 |
Page 87 |
Page 88 |
Page 89 |
Page 90 |
Page 91 |
Page 92 |
Page 93 |
Page 94 |
Page 95 |
Page 96 |
Page 97 |
Page 98 |
Page 99 |
Page 100 |
Page 101 |
Page 102 |
Page 103 |
Page 104 |
Page 105 |
Page 106 |
Page 107 |
Page 108 |
Page 109 |
Page 110 |
Page 111 |
Page 112 |
Page 113 |
Page 114 |
Page 115 |
Page 116 |
Page 117 |
Page 118 |
Page 119 |
Page 120 |
Page 121 |
Page 122 |
Page 123 |
Page 124 |
Page 125 |
Page 126 |
Page 127 |
Page 128 |
Page 129 |
Page 130 |
Page 131 |
Page 132 |
Page 133 |
Page 134 |
Page 135 |
Page 136 |
Page 137 |
Page 138 |
Page 139 |
Page 140 |
Page 141 |
Page 142 |
Page 143 |
Page 144 |
Page 145 |
Page 146 |
Page 147 |
Page 148 |
Page 149 |
Page 150 |
Page 151 |
Page 152 |
Page 153 |
Page 154 |
Page 155 |
Page 156 |
Page 157 |
Page 158 |
Page 159 |
Page 160 |
Page 161 |
Page 162 |
Page 163 |
Page 164 |
Page 165 |
Page 166 |
Page 167 |
Page 168 |
Page 169 |
Page 170 |
Page 171 |
Page 172 |
Page 173 |
Page 174 |
Page 175 |
Page 176 |
Page 177 |
Page 178