research review II-VI lasers produce
powerful green emission Combining a GaN pump source with a novel II-VI structure yields a powerful,efficient green laser
An international research team has constructed a very powerful, highly efficient green source that employs a violet nitride laser to optically pump a II-VI heterostructure. The 150 mW, pulse-driven 543 nm laser that results is a very promising candidate for the green source for low-cost, high-resolution pico- projectors that can be incorporated into smartphones, digital cameras and laptops.
The green laser created by researchers from Ioffe Physical-Technical Institute, Russia, the King Abdulaziz City for Science and Technology, Saudi Arabia, and the Institute of Physics of NAS Belarus, produces a conversion efficiency in excess of 25 percent and a wall-plug efficiency (WPE) of 6 percent. This is comparable to the WPE of second harmonic generation (SHG) lasers, which have values of 6-12 percent, and nearly three times that of green InGaN lasers emitting at 523-525 nm.
Sergei Sorokin from Ioffe Physical- Technical Institute says that the design of the II-VI converters is probably simpler than those employed in SHG laser diodes. What’s more, he claims that the output power of these II- VI lasers promises to exceed that of their InGaN cousins, which have relatively high threshold current densities when operating in the green spectral range. “Additionally, the lasing wavelength of the III-N/II-VI converters can be varied in the wide green range from 520 to 560 nm,” adds Sorokin.
Historically, II-VI lasers have been plagued with short lifetimes. However, Sorokin says that with this wavelength-converting design, device lifetime should be governed by that of the violet nitride laser. “The undoped II-VI optically-pumped laser structures possess long enough lifetime.”
The team have been developing lasers incorporating II-VI structures for several years, and in 2007 they reported a source with five electronically coupled CdSe/ZnSe quantum dot planes that delivered a pulsed output of 65 mW. The latest design produces nearly three times this power, thanks to the introduction of a superlattice graded-index waveguide. This introduces
an electric field, which sweeps carriers that are optically generated in this waveguide into the quantum dots.
Fabricating this waveguide from II-VI materials is very challenging because minor adjustments to the composition of ZnMgSSe produce large changes in lattice constant. “The superlattice graded-index waveguide allows digital variation of composition profile, keeping all the growth parameters unchanged,” says Sorokin. What’s more, strain balancing is possible in this structure.
The team forms its Cd(Zn)Se/ZnMgSSe quantum dot structure by MBE on a GaAs buffer layer. Migration enhanced epitaxy, which is similar to atomic layer epitaxy, is employed to deposit the initial ZnSe layer on GaAs. “We deposit only a part of monolayer during one deposition cycle, due to surface reconstruction peculiarities,” says Sorokin. “The interruption between zinc and selenium fluxes is necessary to allow efficient redistribution of adatoms at the proper places on the surface.”
The team’s green source, which employs a ToPGaN 416 nm laser with a 1W output in pulsed mode (pulse duration of 50 ns and frequency of 1 kHz), has a peak room- temperature output of 154 mW.
Sorokin says that pumping must be performed with ultra-violet LEDs, rather than laser diodes, before it will be possible to make cheap, compact devices based on the marriage of II-Vs and III-Vs. “This, in turn, requires further improvements of the threshold and output characteristics of II-VI optically-pumped laser heterostructures, as well as in the converter design as a whole.”
The team is addressing this issue, and in addition, it has set itself the goals of: Cutting the density of extended defects in the II-VI laser heterostructure to below 104
cm-2 ; reducing the threshold power
density of II-VI laser structures below 1kW/cm2
; and studying device reliability.
S.V. Sorokin et al. Electron. Lett. 48 189 (2012)
I
www.bronkhorst.com - E
info@bronkhorst.com T +31(0)573 45 88 00 - F +31(0)573 45 88 08
Digital Mass Flow and Pressure Meters/Controllers
Gas flows from 0-5 sccm to 0-1670 slm Multi-Gas / Multi-Range, freely programmable ranges and gas types Fast response Pressures from 0-5 to 0-6000 psi High accuracy, excellent repeatability Analog and digital communication (e.g. RS232, DeviceNetTM
)
Elastomer- or metal-sealed Surface mount options available (SEMI standard)
Innovation – Experience – Excellence
March 2012
www.compoundsemiconductor.net 51
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46 |
Page 47 |
Page 48 |
Page 49 |
Page 50 |
Page 51 |
Page 52 |
Page 53 |
Page 54 |
Page 55 |
Page 56 |
Page 57 |
Page 58 |
Page 59 |
Page 60 |
Page 61 |
Page 62 |
Page 63 |
Page 64 |
Page 65 |
Page 66 |
Page 67 |
Page 68 |
Page 69 |
Page 70 |
Page 71 |
Page 72 |
Page 73 |
Page 74 |
Page 75 |
Page 76 |
Page 77 |
Page 78 |
Page 79 |
Page 80 |
Page 81 |
Page 82 |
Page 83 |
Page 84 |
Page 85 |
Page 86 |
Page 87 |
Page 88 |
Page 89 |
Page 90 |
Page 91 |
Page 92 |
Page 93 |
Page 94 |
Page 95 |
Page 96 |
Page 97 |
Page 98 |
Page 99 |
Page 100 |
Page 101 |
Page 102 |
Page 103 |
Page 104 |
Page 105 |
Page 106 |
Page 107 |
Page 108 |
Page 109 |
Page 110 |
Page 111 |
Page 112 |
Page 113 |
Page 114 |
Page 115 |
Page 116 |
Page 117 |
Page 118 |
Page 119 |
Page 120 |
Page 121 |
Page 122 |
Page 123 |
Page 124 |
Page 125 |
Page 126 |
Page 127 |
Page 128 |
Page 129 |
Page 130 |
Page 131 |
Page 132 |
Page 133 |
Page 134 |
Page 135 |
Page 136