research review How to grow defect-free
GaAs nanowires on silicon Scientists have found that employing different growth conditions can improve the properties of gallium arsenide nanowires grown on silicon (111) substrates.
IF you want to use nanowires in optoelectronic devices, they need to have a pure crystal structure without defects such as twins, phase polytypism and stacking faults.
Now a research group at the Australian National University led by Chennupati Jagadish has developed defect-free GaAs nanowires on silicon substrates by employing special growth processes. To determine if it was possible to improve nanowire crystal quality, the scientists, led by Jagadish, grew GaAs NWs on Si (111) substrates using 3 different conditions (Fig. 1). By growing GaAs buffer layers to minimise mismatch in lattice constants and thermal coefficients, the researchers achieved straight GaAs NWs when vertically grown on the silicon substrates.
In collaboration with research groups in the University of Queensland (headed by Jin Zou) and University of Cincinnati, USA (led by Howard Jackson), the scientists then investigated the crystallographic structures and optical properties of the nanowires. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), and micro- and time resolved-
Figure 2.High resolution-SEM images of (a) Standard GaAs NWs with grooved surface, (b) two-temperature grown GaAs NWs and (c) rapidly grown GaAs NWs showing less tapering without any surface defects, respectively: scale bars represent 200 nm and *Y(vn) means yield of vertical NWs; high resolution-TEM images of (d) the standard NWs having twin defects, (e) the two-temperature grown NWs and (f) the rapidly grown NWs showing pure zinc-blende crystal structure and (g) Cross- sectional TEM image of the standard NWs showing truncated triangular shape. The schematic inset shows the evolution of shape change. All scale bars in insets are 5 nm
Figure 3 (a) Plot of NW diameter measured at distance from the top of nanowires and illustration of the change in diameter per unit of NW length. All 3 types of GaAs NWs were measured at each 0.5 µm point; (b) Low temperature (15K)
photoluminescence (µ- /TR-PL) measurements were the main analysis techniques used in the study. Modifying the growth conditions by using two- temperature growth and a rapid growth rate yielded vertical GaAs NWs without surface roughness and structural defects (Fig. 2).
Figure 1: Schematics showing the three- different growth methods
42
www.compoundsemiconductor.net July 2011
The rapid growth rate method resulted in the highest yield of straight and vertical NWs while the two-temperature growth method yielded NWs with the longest exciton life-time (~ 600 ps) and least tapered shape (Fig. 3), desirable
for optoelectronic device applications.
These results show promise for integrating III-V nanowire optoelectronic devices with silicon based
microelectronic devices. The research group at the Australian National University is now working with the collaborators to investigate multiple applications of GaAs NWs as well as other III-V compound semiconductor nanowires for device applications.
Jung-Hyun Kang et al. Crystal Growth & Design
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46 |
Page 47 |
Page 48 |
Page 49 |
Page 50 |
Page 51 |
Page 52 |
Page 53 |
Page 54 |
Page 55 |
Page 56 |
Page 57 |
Page 58 |
Page 59 |
Page 60 |
Page 61 |
Page 62 |
Page 63 |
Page 64 |
Page 65 |
Page 66 |
Page 67 |
Page 68 |
Page 69 |
Page 70 |
Page 71 |
Page 72 |
Page 73 |
Page 74 |
Page 75 |
Page 76 |
Page 77 |
Page 78 |
Page 79 |
Page 80 |
Page 81 |
Page 82 |
Page 83 |
Page 84 |
Page 85 |
Page 86 |
Page 87 |
Page 88 |
Page 89 |
Page 90 |
Page 91 |
Page 92 |
Page 93 |
Page 94 |
Page 95 |
Page 96 |
Page 97 |
Page 98 |
Page 99 |
Page 100 |
Page 101 |
Page 102 |
Page 103 |
Page 104