Monitoring the Thermal Treatment of a Heterogeneous Catalyst Using DRIFTS


Philipp Mueller, Sabrina Conrad, and Ive Hermans, University of Wisconsin – Madison The thermal treatment of a grafted Sn-SiO2 catalyst was monitored in situ using diffuse refl ectance infrared Fourier transform spectroscopy (DRIFTS). Structural changes and organic intermediates could be observed.


Thermal treatment is an important but oftentimes poorly understood step during the synthesis of heterogeneous catalysts. In situ spectroscopic techniques can provide valuable insights into structural changes of such materials upon heating. DRIFTS is an ideal technique for such an application because powder samples can be used without further preparation, high temperatures and pressures can be applied and gases can be fl own over the catalysts easily.


Experimental Conditions The FT-IR spectra were recorded by averaging 32 scans with a resolution of 8 cm-1


using a grafting technique under static vacuum. )4


. Using


the heated environmental chamber inserted into the DiffusIR diffuse refl ection sampling accessory (Pike Technologies; Madison, WI), the environmental chamber was fl ushed with synthetic air at a fl ow rate of ca. 20 mL/min and heated at a rate of 20°C/min up to a temperature of 550°C. Prior to the thermal treatment, the Sn(NMe2 dehydrated SiO2


was deposited on


Figure 2. Spectra recorded at 25°C (black), 100°C (light blue), 200°C (purple), 300°C (dark blue), 400°C (red), 500°C (green) and 550°C (yellow).


band at 3286 cm-1


has been assigned to N-H stretch vibrations of ammonium species that could be formed as intermediates on the silica surface upon heating. The other band at 3656 cm-1


originates from Sn-OH groups that have been formed due to restructuring of the Sn surface species during the calcination [1].


At 200°C another band at 3739 cm-1 is clearly visible. This band stems from the Si-OH


stretch band of isolated silanols [2]. The intensity of this band increases upon further heating, indicating the opening of siloxane bridges on the silica surface.


At 400°C the intensities of the C-H stretch vibrations have further decreased and the vibration at 3286 cm-1


completely disappeared while the Si-OH and Sn-OH stretch bands


were still increasing in intensity. At the fi nal temperature of 550°C, all organic groups have been burned off and the desired and catalytically active Sn sites are present.


Conclusions Figure 1. PIKE DiffusIR diffuse refl ection accessory Results


By applying the environmental chamber and heating the sample up to 550°C, conditions comparable to the ones in conventional calcination ovens could be achieved. Figure 2 shows spectra recorded at different temperatures.


At room temperature intense bands between 2750 and 3000 cm-1


can be assigned to C-H stretch vibrations of the organic Sn precursor. Already at 100°C these bands signifi cantly decreased, while bands at 3286 cm-1


and 3656 cm-1


can be observed which appear. The


The DiffusIR accessory is a valuable tool to understand structural changes in heterogeneous catalysts during thermal treatment. The sequence of formation of intermediates, Sn-OH and Si-OH, species could be observed. The gained insights can potentially be used to improve the synthesis of catalysts.


References


1. P. Larkin, Infrared and Raman Spectroscopy; Principles and SpectralInterpretation, Elsevier Inc, San Diego, 2011.


2. F. Rascón, R. Wischert and C. Copéret , Chem. Sci. 2, 1449-1456 (2011).


INTERNATIONAL LABMATE - JANUARY/FEBRUARY 2017


Page 1  |  Page 2  |  Page 3  |  Page 4  |  Page 5  |  Page 6  |  Page 7  |  Page 8  |  Page 9  |  Page 10  |  Page 11  |  Page 12  |  Page 13  |  Page 14  |  Page 15  |  Page 16  |  Page 17  |  Page 18  |  Page 19  |  Page 20  |  Page 21  |  Page 22  |  Page 23  |  Page 24  |  Page 25  |  Page 26  |  Page 27  |  Page 28  |  Page 29  |  Page 30  |  Page 31  |  Page 32  |  Page 33  |  Page 34  |  Page 35  |  Page 36  |  Page 37  |  Page 38  |  Page 39  |  Page 40  |  Page 41  |  Page 42  |  Page 43  |  Page 44  |  Page 45  |  Page 46  |  Page 47  |  Page 48  |  Page 49  |  Page 50  |  Page 51  |  Page 52  |  Page 53  |  Page 54  |  Page 55  |  Page 56  |  Page 57  |  Page 58  |  Page 59  |  Page 60  |  Page 61  |  Page 62  |  Page 63  |  Page 64  |  Page 65  |  Page 66  |  Page 67  |  Page 68  |  Page 69  |  Page 70  |  Page 71  |  Page 72  |  Page 73  |  Page 74  |  Page 75  |  Page 76  |  Page 77  |  Page 78  |  Page 79  |  Page 80  |  Page 81  |  Page 82  |  Page 83  |  Page 84  |  Page 85  |  Page 86  |  Page 87  |  Page 88