Dealing with scrap iron and steel cargoes and incidents
According to Dr Neil Sanders, the following general points may assist, although no two incidents are the same and each must be assessed to determine the appropriate actions.
1
Measuring hold gases daily should help to identify any reduced oxygen levels, hydrogen, other flammable gases, and carbon monoxide, although gas measurement is not mentioned in the IMSBC Code. Carbon monoxide is a good indicator of smouldering and burning. Gas samples should preferably be drawn from hold sample points, with the sampling tube inserted at least 1 metre into the hold ullage to avoid drawing fresh air into the gas monitor.
Typical ships’ gas monitors are often only effective at measuring flammable gases down to about 10% oxygen. Below that level, a different type of flammable gas sensor will be needed, or a splitter to mix the hold gas with fresh air. With a splitter, of course the true readings must be calculated appropriately, also using readings taken without a splitter.
Some ship’s gas monitors use infrared (IR) sensors for flammable gases, which do not register hydrogen. This could lead to missing a dangerous situation. Therefore, gas monitoring for scrap iron and steel cargoes requires correct equipment and correct usage, which will be difficult to arrange if the vessel is already at sea.
2
Ignition sources should be avoided such as smoking, hot work, paint chipping etc., due to the possibility of flammable gas production, although this is not mentioned in the IMSBC Code. This applies unless a ‘gas free’ situation has been confirmed and is re- checked appropriately over time.
3
In the case of self-heating and / or gas production, the correct approach will depend on the situation. For example, production of excessive amounts of flammable gases e.g., hydrogen will mean that natural ventilation is required to keep below the lowest gas level that can allow an explosion, plus a safety margin, such as a maximum of 20% or 50% of the lower explosive limit (LEL). On the other hand, allowing more air (oxygen) into a hold through ventilation will tend to worsen any self-heating or fire. The correct actions will depend on factors such as the gas readings and temperatures.
4
In the case of a fire, the correct approach again depends on the circumstances. Scrap iron and steel in relatively large pieces (tens of millimetres and above), without finely divided material such as turnings, will usually not ignite, except in extreme circumstances. In this situation fires tend to involve combustible materials within the scrap such as cardboard, plastics, oils etc.
Fires can often be controlled via the hold being closed and un-ventilated to limit oxygen. This is easier if the proportion of combustibles in the cargo is not very high.
However, flammable gases can build up in a hold in a fire situation, or they may exist already e.g., due to hydrogen production. Low oxygen levels in a hold, due to oxidation reactions of the cargo or fire, may prevent explosive mixtures of flammable gases while the hold remains closed. Even so, opening up will introduce air and may risk producing a flammable mixture when air mixes with hold gases, if the flammable gas concentration was high to start with. Therefore, gases should be measured with appropriate equipment, and an assessment made about the correct approach.
Boundary cooling has a limited benefit, if any, for fires in holds. For the cargo itself, the IMSBC Code indicates that water should not be used for firefighting at sea with ferrous metal turnings etc. (Group B), but copious quantities of water may be used in port, having proper regard to the ship’s strength and stability. The entry for scrap metal (Group C) does not mention water. Using water to fight fires in scrap iron and steel cargoes could produce hydrogen and/or its weight could cause strength and stability problems, so it should be considered properly beforehand.
If fuel tanks are adjacent to holds on fire, then consideration should be given to filling them completely (“pressing them up”), to exclude air and prevent fire or explosion in the fuel tank. In extreme cases it may be better to fill fuel tanks with water completely, rather than run the risk of fuel igniting, but usually filling with water can be avoided.
If a fire cannot be controlled without an unacceptable build-up of flammable gases in a hold, then the only alternative may be to discharge the cargo. Once discharged, it can be spread out in a layer ashore and doused with water to deal with fire and self-heating.
After controlling a fire in a hold, some smouldering may continue, even if the oxygen level remains low. Therefore, suitable precautions should be put in place before opening a hold, to deal with any flare-up that may occur.
If a fire involves finely divided iron or steel, such as turnings, then the approach may be similar to that above, but the fire can potentially burn very hot. The same potential issues of flammable gas build-up, explosion risks and ventilation apply, particularly if hydrogen is produced by oxidation with water.
THE REPORT | MAR 2024 | ISSUE 107 | 59
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46 |
Page 47 |
Page 48 |
Page 49 |
Page 50 |
Page 51 |
Page 52 |
Page 53 |
Page 54 |
Page 55 |
Page 56 |
Page 57 |
Page 58 |
Page 59 |
Page 60 |
Page 61 |
Page 62 |
Page 63 |
Page 64 |
Page 65 |
Page 66 |
Page 67 |
Page 68 |
Page 69 |
Page 70 |
Page 71 |
Page 72 |
Page 73 |
Page 74 |
Page 75 |
Page 76 |
Page 77 |
Page 78 |
Page 79 |
Page 80 |
Page 81 |
Page 82 |
Page 83 |
Page 84 |
Page 85 |
Page 86 |
Page 87 |
Page 88 |
Page 89 |
Page 90 |
Page 91 |
Page 92 |
Page 93 |
Page 94 |
Page 95 |
Page 96 |
Page 97 |
Page 98 |
Page 99 |
Page 100 |
Page 101 |
Page 102 |
Page 103 |
Page 104 |
Page 105 |
Page 106 |
Page 107 |
Page 108 |
Page 109 |
Page 110 |
Page 111 |
Page 112 |
Page 113 |
Page 114 |
Page 115 |
Page 116 |
Page 117 |
Page 118 |
Page 119 |
Page 120 |
Page 121 |
Page 122 |
Page 123 |
Page 124 |
Page 125 |
Page 126 |
Page 127 |
Page 128 |
Page 129 |
Page 130 |
Page 131 |
Page 132