STEEL SOLUTIONS for tableting S
Lee Wardall reveals the criteria that must be met for steel products to be successfully deployed in tableting tools
teel qualities used in the manufacturing of tablet compression tooling can be defined in many ways. However, the key characteristics are generally the cleanliness of the steel, the quality and homogeneity of the microstructure, and the distribution of the carbides within the steel. Tere are six main
requirements for steels used in the manufacturing of compression tooling. Te first is abrasive wear resistance. Tis is resistance to abrasion and erosion. More carbides and higher hardness improve tools’ wear resistance. Vanadium, molybdenum, chromium and carbon can also contribute to improved wear resistance. Next on the list is toughness – i.e. good resistance to chipping. Te toughness of the steel can be described as the ability to absorb impact energy without breaking and/or chipping. An increased volume of silicone improves toughness of the steel. Fatigue strength is the ability of the tooling to withstand repeated load cycles without cracking or chipping. A large uneven distributed carbide structure is detrimental and significantly reduces the toughness, fine carbides, evenly dispersed are highly beneficial. Te third requirement is high compressive strength. Tis
www.scientistlive.com
is the ability to withstand a constant load without deforming or breaking. Molybdenum contributes to improving the compressive strength of the punches.
Through hardening properties Good through hardening properties is the next requirement. Temper resistance is the steel’s ability to maintain hardness as the surface temperature becomes elevated while having surface treatments applied or while in use. Molybdenum and tungsten contribute to temper resistance. High hardness after high
temperature tempering and good stability in hardening is also important. Harden ability is the ability of the steel to through harden and form martensite. Correct heat treating is essential. Carbon is also a key element in hardening. Te final requirement is
that of corrosion resistance. Tis is the steel’s ability to resist the corrosive effects of the products it comes into contact with and the environment and conditions they are used and stored in. Te chromium contact of the steel has a considerable impact on the steel’s resistance to corrosion.
The ESR process A key process involved in the production of quality steels is electroslag remelting (ESR). Tis produces very clean homogenous steel by passing an ingot through reactive molten slag, removing the impurities and producing a refined structure. Tis process continues until the impurities are removed and a
clean homogenous structure is produced. Te steels produced are stringently measured and analysed against many standards, including ASTM, DIN, JIS and ISO, to make sure the steels’ cleanliness and quality requirements are met. Adamus HT recognises the importance of the steels’ chemical composition and therefore delivers this information on every tooling shipment in the form of a Certificate of Conformity given independently by the steel supplier.
Standard and speciality steels Adamus HT uses steel grades that fulfil all the abovementioned requirements and it supplies them only from the world’s leading steel producers. Besides the standard steel grades used by all compression tooling suppliers, the company also offers a series of different speciality steels that can solve the tableting problems with abrasive, sticky and corrosive products as well as products that require higher compression forces than recommended due to the tablet size and dimensions.
For more information ✔ at
www.scientistlive.com/eurolab
Adamus HT uses steel grades that meet all technical requirements for use in tableting applications
Lee Wardall is director of customer services at Adamus.
www.adamus.co.uk
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46 |
Page 47 |
Page 48 |
Page 49 |
Page 50 |
Page 51 |
Page 52 |
Page 53 |
Page 54 |
Page 55 |
Page 56 |
Page 57 |
Page 58 |
Page 59 |
Page 60 |
Page 61 |
Page 62 |
Page 63 |
Page 64 |
Page 65 |
Page 66 |
Page 67 |
Page 68 |
Page 69 |
Page 70 |
Page 71 |
Page 72 |
Page 73 |
Page 74 |
Page 75 |
Page 76 |
Page 77 |
Page 78 |
Page 79 |
Page 80 |
Page 81 |
Page 82 |
Page 83 |
Page 84