60 | Talking Timber: Wind Turbines
WOOD AND WIND TURBINES
Martin Ansell discusses the application of wood in the construction of modern wind turbines and the environmental advantages of selecting wood
Modern multi-megawatt wind turbines are mostly horizontal axis machines with the generator set mounted on a steel tower. The aerofoil turbine blades are usually manufactured from glass- or carbon fibre-reinforced plastic (GFRP or CFRP) with the rotor hub connected horizontally to the generator. Wind speeds increase with height above the ground and the power generated is proportional to the swept area of the blades. Hence, tall towers
and long blades maximise power output. Wind turbines are intended to have a design life of
approximately 25 years. There are now approximately 2,000 wind farms in the UK with about 1,500 located onshore and 500 offshore. Turbine blades experience aerodynamic and gravitational loads which result in progressive fatigue damage, so blades must be replaced well before catastrophic failure is a possibility. Fibre-reinforced plastics (FRPs) are difficult to recycle, and blades are often buried in landfill sites. Recycling options include chemical methods such as depolymerization and pyrolysis to produce the basic constituents of polymers, fuels and fertilisers. Alternatively, the FRPs can be ground up or shredded and used as fillers and reinforcements for concrete and asphalt. Both options are complex and expensive.
An alternative approach is to manufacture turbine blades and towers from wood, which is more recyclable. In the last two years Voodin blades (
https://voodin-blades.com) have been manufactured in Germany from laminated veneer lumber, manufactured by Stora Enso from birch veneer sourced in Finland. To date 19.3m blades have been installed on a wind turbine and 50m-plus blades for a 4.2MW turbine are being developed with Senvion of India (
https://www.senvion.in). The Swedish company Modvion (
https://modvion.com) manufactures laminated wood wind turbine towers, which are delivered to site in sections. In 2024 a Vestas V90-2.0MW wind turbine with a Modvion tower was installed in Sweden. The tower is 105m tall and the total height of the wind turbine is 150m including blades. Heavy steel towers are usually shipped by road as single welded units whilst shorter laminated wood sections can be assembled on site.
In the 1980s Jim Platts and Mark Hancock at Gifford
Technology, Southampton developed laminated wood turbine blades using rotary peeled African mahogany (Khaya ivorensis) veneer. The blades were vacuum bagged in two half blade moulds and bonded together with an internal shear web. The bonded wood technology was developed originally for boatbuilding by Gougeon Brothers in the US using the WEST epoxy system for bonding veneers. Concurrently, a long-term
TTJ | Spring 2026 |
www.ttjonline.com
Dr Martin P Ansell, FIMMM is honorary reader in Materials at the Department of Architecture and Civil Engineering at the University of Bath
Below: Wind Energy Group wind turbines in California erected in 1986 (MS-2) and 1988 (MS-3) with wood/epoxy blades
fatigue testing programme, funded by the UK government and the EU, was carried out by the author at the University of Bath to generate comprehensive fatigue design data for wood laminates under cyclic and complex loads. Gifford Technology expertise was subsequently transferred to several companies, including the Wind Energy Group (Taylor Woodrow) in a series of takeovers and became the property of Aerolaminates who manufactured laminated wood-epoxy wind turbine blades on the Isle of Wight. In 1998, following the takeover of Aerolaminates, NEG Micon built a new facility for the manufacture of hybrid laminated wood/ carbon fibre-reinforced hybrid blades and in 2003 developed a commercial blade for a 110m diameter rotor for multi-megawatt turbines. However, as blade diameters and turbine capacities increased, aerodynamic and gravity loads also increased. As a result, companies such as Vestas in Sweden took advantage of the high stiffness and strength of CFRP to manufacture blades and used balsa wood as a core material to space the skins and resist shear loads. ■
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46 |
Page 47 |
Page 48 |
Page 49 |
Page 50 |
Page 51 |
Page 52 |
Page 53 |
Page 54 |
Page 55 |
Page 56 |
Page 57 |
Page 58 |
Page 59 |
Page 60 |
Page 61 |
Page 62 |
Page 63 |
Page 64 |
Page 65 |
Page 66 |
Page 67 |
Page 68 |
Page 69