Anti-corrosion systems deployed in Saudi Arabia
A challenging application in the Middle East was no problem for one coating expert, as Sander Hofstee reveals.
F
ollowing a successful partnership lasting more than a decade, two organisations have once again worked together to successfully deploy a new coating system in the Middle East.
Te Dutch company Stopaq first introduced
its non-crosslinkable visco-elastic technological system to Saudi Aramco, with the support of the AlSuwaiket group, in 1998. As a result of this ongoing partnership, Stopaq
(now part of the Seal For Life group) was recently invited by Saudi Aramco to introduce its factory- applied glass reinforced epoxy (GRE) system. Te system consists of a visco-elastic ‘primer’
layer with a GRE mechanical protective top layer directly applied on top. Since the introduction of Stopaq factory-applied linepipe coating systems, this new coating has been primarily used on pipelines in highly concentrated city areas, horizontal directional drilling situations and at refineries. Clients and contractors discovering the
advantages of the system are now also using it on big-diameter thrust boring applications and protection of uncoated and fusion bonded epoxy- (FBE) coated pipes exposed to corrosive conditions. Te most recent challenge was found in Saudi Arabia, where Seal For Life Middle East (formerly known as Stopaq Middle East) was invited to coat pipes on site at the new-build Dhahran Techno Valley. Te project involved the coating of 12-inch diameter pipes that each had an individual length of 26.2m and were to be used for thrust boring. Te pre-coated FBE pipes were already in possession of Saudi Aramco and stored in the company’s yard. For this project the equipment was brought to site, allowing the coating to take place directly next to the trench, thereby minimising any logistical activities that could damage the pipes. As a result of the very low coating surface tension, Stopaq’s first visco-elastic layer shows excellent wetting on all surfaces including – but not limited to – steel, PE, PP and FBE. Tis combination of low surface tension and the fluid-like behaviour of the coating causes full impregnation of the complete surface into the finest pores, which favours corrosion prevention.
34
www.engineerlive.com
Fig. 1. Applying the coating on-site reduces the opportunity for pipes to be damaged.
Te coating does not require an anchor profile to ensure that adhesion occurs, unlike the commonly used epoxy coating materials or adhesives. Te application of this primer layer can take place after the minimum surface preparation, ST2 derusting.
End of any weak spots
Te application of the field joint coating system consists of the same materials as the mainline coating, so the primary layer also consists of the same non-curing, non-crosslinkable, fully amorphous, liquid-like polymer composition. Tis makes the two layers flow together after application at all times and in any circumstance. It also means there are no weak links and removes the need to preheat and provide anchor pattern for optimal adhesion. Te abovementioned method is known
as ‘Stopaq FAST’ (Factory-Applied Stopaq Technology). In summary, applying the Stopaq FAST system overcomes a number of issues, including high soil stress, stress corrosion, hydrogen- induced corrosion and undercreep corrosion. l
For more information ✔ at
www.engineerlive.com/iog
Sander Hofstee works for Seal For Life Industries in the Netherlands.
www.sealforlife.com
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46 |
Page 47 |
Page 48 |
Page 49 |
Page 50 |
Page 51 |
Page 52 |
Page 53 |
Page 54 |
Page 55 |
Page 56 |
Page 57 |
Page 58 |
Page 59 |
Page 60 |
Page 61 |
Page 62 |
Page 63 |
Page 64 |
Page 65 |
Page 66 |
Page 67 |
Page 68 |
Page 69 |
Page 70 |
Page 71 |
Page 72 |
Page 73 |
Page 74 |
Page 75 |
Page 76 |
Page 77 |
Page 78 |
Page 79 |
Page 80 |
Page 81 |
Page 82 |
Page 83 |
Page 84 |
Page 85 |
Page 86 |
Page 87 |
Page 88 |
Page 89 |
Page 90 |
Page 91 |
Page 92 |
Page 93 |
Page 94 |
Page 95 |
Page 96 |
Page 97 |
Page 98 |
Page 99 |
Page 100