The stress of grinding or welding
accessories that are in use?” The answer is no, not without the permission of the Original Equipment Manufacturer (OEM). When out in the field it may be tempting to grind or weld components or accessories such as hooks, shackles or chain slings for the purpose of quick repair or even to modify it for a specific task. However, grinding and welding can cause stress raisers. These are areas where stress is significantly higher than the surrounding area, which can lead to failure. OEMs may permit grinding out minor surface defects, such as die casting flash (excess material), but this is usually addressed in the manufacturing process. If so, they should provide guidelines in their user instructions, but they will not permit welding or any other modification, without their knowledge and written consent. Additions or changes to a product once
O
placed on the market or in service, will need to be approved by the OEM and verified by a competent person following the work carried out and before use. Effectively, this is the modification of lifting equipment after manufacture and once placed on the market or in service.
Grinding Grinding of forged or cast steel accessories and components, such as shackles, is not recommended due to the potential to weaken the material and introduce stress risers. While grinding can remove surface imperfections, excessive grinding can disrupt the grain flow and introduce stress concentrations, which can lead to premature failure.
Any grind marks found should be treated as defects affecting the safety of the equipment and it is the competent person’s decision whether they are severe enough to fail the equipment. Grinding is sometimes seen in ad hoc sling assemblies of various accessories where numerous Working Load Limits (WLLs) may be present. This is usually carried out to reduce the risk of misidentification of the sling assembly’s WLL, which should be identified by a sling tag. It
10 | July/August 2026 |
www.hoistmagazine.com
ne of the frequently asked questions we receive at LEEA is: “Can I grind and weld steel components and
Ben Dobbs
Technical Committee
Ben Dobbs, head of global standards and legislation at the Lifting Equipment Engineers Association (LEEA), answers a frequently asked question about grinding and welding.
If components or accessories are welded
may also occur on a runway that may have been fitted with a hoist of higher WLL than that marked on the beam itself.
Welding Welding is also not recommended on components or accessories, as it can significantly alter the material properties of the metal being worked. It can potentially lead to reduced strength and increased risk of failure, especially in critical applications such as lifting operations. A common example in accessories is seen
where a shackle pin is welded to the body to create a permanent fitting. Where this has been carried out, LEEA would assume that a risk assessment identified that there was a risk of the pin unscrewing, hence the weld. This may not, however, reduce the risk sufficiently, and the company in question carrying this out would be held accountable for not selecting equipment fit for the application. It is highly likely that the reasoning behind this may breach legislation due to demonstrable incompetence and poor selection of equipment. A nut and cotter type pin or other type of mechanical securing component would be the appropriate choice. Should the weld result in failure and injury, the enforcing authorities may take a very dim view of this although it is a common practice.
after leaving the OEM, then the owner of the equipment will need to accept full responsibility and will also need to hold comprehensive documented evidence – including (but not limited to) OEM’s permission in writing, risk assessment, welder qualifications, welding specifications and procedures, test records and full traceability. Manufacturers doing this will need to meet the supply legislation requirement for new products and be able to provide the evidence that the complete product is safe to use. Grinding or welding carried out after initial manufacture is not recommended for the above reasons. Competent persons would normally quarantine or condemn components that have been modified due to their training. They would need to see evidence in writing to pass them. Find the answers to more frequently asked technical questions at LEEA’s FAQ page.
ABOUT LEEA
The Lifting Equipment Engineers Association (LEEA) is established across the globe as the leading representative body for all those involved in the lifting industry worldwide. It is the respected and authoritative
representative body for its members who work in every aspect of the industry, from design, manufacture, refurbishment and repair, through to the hire, maintenance and use of lifting equipment. The Association has played a key role in this specialised field for over 80 years, from training and standards setting through to health and safety, the provision of technical and legal advice, and the development of examination and licensing systems. LEEA represents its members at the highest levels across a range of both public and private bodies, including various government departments, as well as nationally and internationally recognised professional and technical institutions.
www.leeaint.com @LEEA_INT
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46 |
Page 47 |
Page 48 |
Page 49 |
Page 50 |
Page 51 |
Page 52 |
Page 53 |
Page 54 |
Page 55 |
Page 56 |
Page 57 |
Page 58 |
Page 59 |
Page 60 |
Page 61 |
Page 62 |
Page 63 |
Page 64 |
Page 65 |
Page 66 |
Page 67 |
Page 68 |
Page 69 |
Page 70 |
Page 71 |
Page 72 |
Page 73 |
Page 74 |
Page 75 |
Page 76 |
Page 77 |
Page 78 |
Page 79