New Possibilities for High Strength Aluminum


Traditionally cast in green sand, A206 aluminum may be a viable alloy for permanent mold castings. YEMI FASOYINU, CANMET MATERIALS, HAMILTON, ONTARIO, CANADA; DAVID WEISS, ECK INDUSTRIES INC., MANITOWOC, WISCONSIN; AND JITEN SHAH, PRODUCT DEVELOPMENT & ANALYSIS LLC, NAPERVILLE, ILLINOIS


ing and Revert Reduction Technol- ogy (E-SMARRT) program, which included a project lead by Canmet Materials (CMAT), Hamilton, Ontario, Canada, on permanent mold casting light metal alloys. CMAT focused specifically on alloys that were considered difficult to pour in a


T


he U.S. Department of Energy funded a number of proposals in 2004 under the Energy Saving Melt-


permanent mold but offered signifi- cant energy savings by reducing revert (or returns). A206 is one of the highest strength


structural alloys. Yield strengths in excess of 45 ksi are routinely achieved in the T71 temper. It has very good high temperature properties with little reduction in strength up to 350F (177C), making it an ideal alloy for cylinder heads and other elevated temperature applications. When poured into a permanent


mold, however, A206 has a tendency for hot tearing, which is caused by thermal contraction in the late stages of solidification. Because of this diffi- culty, A206 most often is cast in green or chemically bonded sand molds. A recent research project aimed to estab- lish processing parameters for A206 in permanent mold castings that prevent hot tearing for structural components in automotive and other applications.


Overcoming Obstacles in Simulation


When working with the 200 series of aluminum alloys, chemistry control is more important than with 300 series aluminums. Iron and silicon levels need to be minimized to achieve the expected properties. Impurities from insufficiently cleaned crucibles or improperly mixed alloys can lead to unsuitable results. Metalcasters must ensure tools and ladles are clean. Process controls to minimize changes in chemistry also are essential. In 200-series alloys, mechanical


Fig. 1. The bracket casting was selected because its geometry was typical of structural components.


properties depend on controlling the iron and silicon levels in the alloy. In A206, iron levels need to be con- trolled to less than 0.1% and silicon levels to less than 0.05%. Castings made with specified chemistries and solidification rates typical of the permanent mold process can develop yield strengths of 50 ksi coupled with double digit elongation. To research the ability to cast A206


September 2014 MODERN CASTING | 31


Page 1  |  Page 2  |  Page 3  |  Page 4  |  Page 5  |  Page 6  |  Page 7  |  Page 8  |  Page 9  |  Page 10  |  Page 11  |  Page 12  |  Page 13  |  Page 14  |  Page 15  |  Page 16  |  Page 17  |  Page 18  |  Page 19  |  Page 20  |  Page 21  |  Page 22  |  Page 23  |  Page 24  |  Page 25  |  Page 26  |  Page 27  |  Page 28  |  Page 29  |  Page 30  |  Page 31  |  Page 32  |  Page 33  |  Page 34  |  Page 35  |  Page 36  |  Page 37  |  Page 38  |  Page 39  |  Page 40  |  Page 41  |  Page 42  |  Page 43  |  Page 44  |  Page 45  |  Page 46  |  Page 47  |  Page 48  |  Page 49  |  Page 50  |  Page 51  |  Page 52  |  Page 53  |  Page 54  |  Page 55  |  Page 56  |  Page 57  |  Page 58  |  Page 59  |  Page 60  |  Page 61  |  Page 62  |  Page 63  |  Page 64  |  Page 65  |  Page 66  |  Page 67  |  Page 68  |  Page 69  |  Page 70