• • • BATTERIES & CHARGERS • • • Quality control under the microscope

Why battery manufacturers need to embrace laser induced breakdown spectroscopy (LIBS). Written by Dr Kay Scheffler, Dr Konstantin Kartaschew, and Dr James DeRose, Leica Microsystems

rate (CAGR) of 13.0% from 2020 to 2027 [1]. Fast-rising demand for electric vehicles is one of the market’s main drivers, but there are other hotspots of growth, including the rise in renewable energy installations, such as photovoltaic panels, and greater acceptance of Li-Ion batteries for use in various devices across the medical sector, as well as more traditional uses in portable consumer electronics. Significant improvements in the performance of Li-


Ion batteries have helped to drive their growing use across the spectrum of industry sectors, but issues remain that have prevented further growth of the market. There are still concerns about risk of overheating, in particular when Li-Ion batteries are charged too quickly – a major issue in electric vehicles where rapid charging is crucial. Their short lifetime is also an issue, with many Li-Ion batteries lasting less than 1,000 charge/discharge cycles [2,3]. In many cases these issues can be rectified at the quality control stage of the manufacturing process. Overheating during use can often be traced back to the presence of metal particles in the electrodes, fuel-cell separators, and other parts of Li-Ion batteries. These particles lead to internal short circuits, which can cause overheating, a decrease in the battery capacity and lifetime or, in extreme cases, result in a fire [4-6]. With demand for their products rocketing, the challenge for battery manufacturers is to ensure their QA/QC procedures are robust enough to capture these impurities, but are not so arduous as to slow down the manufacturing process or lead to significant additional expenditure.


One of the fundamental issues facing manufacturers is that established methods of detecting impurities in Li-Ion batteries are complex, time-consuming, and very difficult to integrate into the production line [7]. The process normally used for quality control processes in industrial


he global lithium-ion (Li-Ion) battery market was valued at US$ 32.9 billion in 2019 and is expected to grow at a compound annual growth

manufacturing environments is energy dispersive x- ray spectroscopy (EDS) using a scanning electron microscope (SEM). SEM-EDS enables researchers to visually inspect a material, using a microscopy technique that generates images with high resolution and sharp contrast, and identify its local composition with elemental spectroscopic analysis. SEM-EDS often requires special sample preparation and transfer of the sample into a vacuum for observation and analysis – a time consuming and technically challenging process. In battery manufacture and QC, SEM-EDS also has some practical drawbacks concerning the detection of the most important element in rechargeable battery technology: lithium (Li) [7]. Additionally, as it is a complex imaging method, SEM-EDS is very difficult to incorporate directly into the production line. This fact means samples need to be sent off of the line to be analyzed, taking hours or possibly even days before the results are available, holding up the production process and leading to significant time and budget implications. Methods which are easier to incorporate into the

production line, like x-ray fluorescence (XRF) and glow discharge optical emission spectrometry (GD- OES) have other disadvantages. XRF cannot detect accurately light elements like Li [8,9] and GD-OES often causes significant damage to the sample and can be difficult to use with insulating materials [9-11].


There is now a new approach coming to the fore in battery manufacture and other industrial applications: a combination of optical microscopy and laser induced breakdown spectroscopy – or LIBS – to achieve visual and chemical sample information in much reduced time. The LIBS process, which enables material composition analysis, sees a high-energy laser pulse strike a targeted area of the material surface, the energy of which is absorbed, causing local area ablation and crater formation. A plasma is induced and then immediately broken down, leading to light emission, with the elemental line spectra detected

and elements thus identified.

Because this approach does not require use of a SEM, many of the most time-consuming steps are eliminated from the process: no additional sample preparation is required before analysis; samples don’t need to be observed in a vacuum, so dry or wet samples in air can be analyzed; and there is no relocation of the region of interest on the sample or adjustment of the system after sample transfer. Results are available in seconds, meaning analysis can be undertaken quickly as part of the quality control process, without needing to use laboratory support – also significantly reducing cost incurred. Leica Microsystems itself has invested significant amounts of time and resources in this space in recent years, because we believe in the future of this technology. The DM6 M LIBS system from Leica Microsystems was designed specifically for industrial applications like battery manufacturing to deliver faster results, when speed as well as accuracy are paramount for long-term success.


Many industries have not embraced LIBS yet, perhaps because SEM-EDS, XRF, or GD-OES are the accepted status quo solutions. Indeed, in product development, quality control and failure analysis – in every sector but especially in battery manufacturing – obtaining reliable results and achieving the desired product quality must always be the priority. But industrial manufacturers must not let the desire to stick with the ‘tried and tested’ get in the way of progress or deny them significant gains in productivity and profitability. SEM-EDS and other techniques still add great value in certain applications, but for rapid, accurate quality control on a fast-moving production line, manufacturers should consider optical microscopy and LIBS – when they’ve seen the benefits it can bring, they will not look back. For sources cited in text, please go to:


Page 1  |  Page 2  |  Page 3  |  Page 4  |  Page 5  |  Page 6  |  Page 7  |  Page 8  |  Page 9  |  Page 10  |  Page 11  |  Page 12  |  Page 13  |  Page 14  |  Page 15  |  Page 16  |  Page 17  |  Page 18  |  Page 19  |  Page 20  |  Page 21  |  Page 22  |  Page 23  |  Page 24  |  Page 25  |  Page 26  |  Page 27  |  Page 28  |  Page 29  |  Page 30  |  Page 31  |  Page 32  |  Page 33  |  Page 34  |  Page 35  |  Page 36  |  Page 37  |  Page 38  |  Page 39  |  Page 40  |  Page 41  |  Page 42  |  Page 43  |  Page 44  |  Page 45  |  Page 46  |  Page 47  |  Page 48  |  Page 49  |  Page 50  |  Page 51  |  Page 52