Coating & Laminating ‘Edge encapsulation’ increases line
speed and reduces coat weight SAM North America uses an EDI Feedblock from Nordson to more than double the line speed in extrusion coating of PLA and reduce coat weight by 40%.
echnologies developed by SAM North America and Nordson Corporation have made it possible to increase throughput and reduce coat weight in the extrusion coating of biopolymers such as PLA by encapsulating the edges of the coating with LDPE.
T
While conventional coextrusion yields two or more materials in horizontal layers, special encapsulating inserts developed by Nordson for its coextrusion feedblock make it possible to extrude additional material along either edge of this horizontal structure. Using this technique, SAM North America has found that encapsulating a PLA coextrusion with edges of LDPE makes it possible to offset deficiencies of PLA – in particular its low melt strength – that have limited its melt curtain stability, draw- down ratio, line speed, and coat weight. “Using LDPE edge encapsulation on our pilot line, we have achieved line speeds in excess of 1200 fpm (366 mpm) with PLA, as against less than 600 fpm (183 mpm) with PLA alone,” said Ed Lincoln, vice president of extrusion sales at SAM North America. “We have seen coat weight reduced from 16 gsm to less than 10 gsm.”
The high melt strength of LDPE has helped make this polymer by far the most widely used in extrusion coating. “For processors wishing to replace some portion of their LDPE usage with biopolymers, a main obstacle has been that their lower melt strength causes extreme neck-in and edge instability at desirable line speeds,” said Sam Iuliano, chief technologist for Nordson’s EDI extrusion die and feedblock business. “By introducing a higher-melt strength material on each edge of the melt curtain, edge encapsulation minimizes the processing limitations posed by many biopolymers.”
Neck-in is the tendency of the polymer web to become narrower as tension is applied when it exits the die. The result is a build-up of material along the edges of the web, or ‘edge bead’ that must subsequently be trimmed away as scrap. To ensure that this edge bead consists of the lowest-cost polymer in the
Schematic above, with upper die and feedblock halves removed, shows encapsulation achieved with Nordson feedblock insert (circled); schematics below show a new EDI EPC die, with encapsulating polymer introduced in the die rather than in the feedblock.
coextruded structure, Nordson has developed customizable feedblock inserts that introduce flow of the low-cost polymer only at the edges of the structure.
The combined materials are then distributed to the final target width in the flow channel or manifold of the die.
While the encapsulation inserts can be readily retrofitted into existing EDI feedblocks, Nordson offers new EDI dies equipped with the EPC deckle system, which can be adjusted to reduce edge bead formation, and a melt flow system in which the edge encapsulation polymer is introduced in the die rather than
in the feedblock. The port for introducing the encapsulation polymer moves in concert with the deckle mechanism.
“By introducing the encapsulation polymer at this point in the process, the interface between it and the core structure is more defined and the transition overlap between the encapsulation material and the biopolymer material is reduced,” said Mr. Iuliano. “The die limits the formation of edge bead and reduces the amount of edge trim.”
Xwww.sam-na.com.
Xwww.nordsonpolymerprocessing.com
12
November 2021
www.convertermag.com
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46