Feature Article Introduction


investment casting and can have major issues with shell quality and scrap. The question of when a ceramic shell is dry has confronted foundrymen since the introduction of the shell mould. Funk and Wagnalls Standard College Dictionary1


D


Drying of Ceramic Shells by Manuel Guerra and Gavin Dooley, REMET


rying of shell systems is one of the most topical areas of ceramic processing within


defines dry as “devoid of


moisture; not wet or damp”. However, when is a shell (or individual dipcoat) “devoid of moisture”? The answer to this question is not always straightforward. Furthermore, does a coat need to be fully dry? Several different methods have been


used over the years to try to determine dryness. These include re-dip indicators, electrical conductivity, humidity measurements,


thermocoupling the


wax pattern, checking the temperature, and weighing moulds. Many of these methods have merit, but what may work well in one foundry will not always transfer to another. There are many factors to consider (ie.; shell throughput, room size, part configuration, etc.). In this paper, a simple configuration was chosen, so that consistent results would be obtained. Also, only water-based colloidal silica binder will be addressed. However, some of the same principles will hold true for non-aqueous systems. Drying has been studied for many


years, as it is critical in the manufacture of most ceramic bodies. Most monolithic ceramic bodies must have moisture removed in a very controlled manner, or severe cracking or warping can occur. Fortunately, the sequence of putting one dip on at a time allows for much greater flexibility in drying, as the slurry layer is thin and spread over a wide area. Also, the stucco layer acts to slow down the rate of dry on each individual dip by covering much of the surface of the slurry. Nevertheless, low relative humidity and/or excessive air movement can cause cracking on the first several


22 ❘ June 2020 ® Figure 1: Drying of ceramic shells


dips. One reason often given for this occurring is “over drying”. However, what most people


perceive as over drying is really a case of drying too rapidly. In addition, after the coat is dry or nearly dry, a large or rapid temperature


change can cause wax


expansion which can crack the coating. A graphic illustration of the stages of drying is shown in Figure 1. Part A of Figure 1 shows a group of particles separated by a large amount of water, which would be the case when a cluster has just been dipped. Part B is when some of the water has been removed. Some shrinkage has occurred, and many of the particles have started to touch. In Part C, drying shrinkage has stopped, as all the particles have made at least some contact with other particles. A great deal of water is left in the pores and at interparticle contacts. In Part D, most of the readily accessible water is gone. Some liquid in small capillaries


remains, along with physically adsorbed water.


If the drying rate is too fast, stresses


occur in the ceramic. If these stresses are large enough, cracking can occur. In some instances, the cracking does not create a major defect, but many times it will (ie.; buckle, lifting, etc.). When the defect occurs a long time after the part has been dipped, over drying is usually cited as the cause. However, unless the dried cluster has been subjected to new stresses, the residual stress from too fast a dry rate is almost always the problem. It has long been known that colloidal


silica binders do not form strong bonding networks when gelled (by acids, bases, or salts). The binder must set (by drying) to yield optimum bonding strength. If colloidal silica is not allowed to totally set, a certain loss in strength will occur. The amount of the loss will depend on how much moisture is left in the ceramic when it is re-dipped.


Page 1  |  Page 2  |  Page 3  |  Page 4  |  Page 5  |  Page 6  |  Page 7  |  Page 8  |  Page 9  |  Page 10  |  Page 11  |  Page 12  |  Page 13  |  Page 14  |  Page 15  |  Page 16  |  Page 17  |  Page 18  |  Page 19  |  Page 20  |  Page 21  |  Page 22  |  Page 23  |  Page 24  |  Page 25  |  Page 26  |  Page 27  |  Page 28  |  Page 29  |  Page 30  |  Page 31  |  Page 32