Ductile & CG Iron Casting Skin - Evaluation, Effect on Fatigue Strength & Elimination Phase II (09-10#01)


Coordinator: Ohio State University and AFS Cast Iron Divi- sion (5)


The elimination of the flake skin is one of the key elements of unlocking the full design potential of Compacted Graphite Iron (CGI). Capitalizing on the results of a previously AFS sponsored effort 04-05#02, “Study of the Effect of the Cast- ing Skin on the Tensile Properties of Light Weight Ductile Iron Castings”, the Department of Materials Science and Engineering at The Ohio State University (OSU) propos- es to conduct research with the goal of understanding the mechanism of formation of casting skin in CGI, evaluating its effect on selected mechanical properties, and developing the methodology for its complete elimination. The results of this research will be of immediate applicability to the industry without major capital investment.


The research strategy is designed to develop the knowledge required to improve and ultimately eliminate skin quality of CGI castings and to generate data on its impact on the static mechanical and fatigue properties of CGI, as well as on the efficiency of shot blasting in improving these properties. Ad- ditionally, the study may help in the definition of the minimum thickness of the layer that must be removed by machining to avoid negative skin quality effects. The research will capitalize on the experience in the characterization of casting skin ac- cumulated in the Virtual Solidification and Casting Laboratory (VisionCast) at OSU.


The success of this investigation will rely on the completion of extensive experimental work that will provide critical data required in the understanding of casting skin formation and elimination. The developed correlations between process variables, casting skin quality and mechanical properties will provide the impetus to further expand the applications of CGI. During Phase I, the mechanism for skin formation and test specimens design was validated. During Phase II fatigue specimens will be cast and influence of skin formation of fatigue will be determined. Also, potential actions to reduce or eliminate skin formation will be investigated.


Status Update: The Final report was being written and Phase II has begun. Those wishing further information on the project should contact Prof. Doru Stefanescu, The Ohio State Univer- sity, at stefanescu.1@osu.edu


Ductile Iron Structure/Property Optimization & Enhancement Phase I (09-10#02)


Coordinator: Stork CRS and AFS Cast Iron Division (5), DIS and Consortium


ASTM A536 contains examples of the yield strength, tensile strength and percent elongation relationships expected in duc- tile cast iron. Frequently, both castings and test bars will exhibit mechanical properties that are significantly better than the mini- mums expected as indicated in the ASTM specification. One ex- ample is the information generated by the researchers from test- ing a pearlitic ductile iron expected to have mechanical strength properties that would be consistent with the pearlitic 80-55-06 grade, but exhibiting high ductility of almost 15% elongation.


To our knowledge, research work has not been conducted to determine what is required to consistently achieve such proper- ties with this extent of ferrite. It is known that strengthening mechanisms in metal include solid solution strengthening with both substitutional and interstitial elements. Work hardening is another means to strengthen metals. Phase transformation, pre- cipitation hardening and grain refinement are still other mecha- nisms utilized to strengthen metals.


This study will characterize the graphite and other factors that con- trol the matrix mechanical properties that are independent of nod- ule count, size and morphology. The characterization will include tensile and compression testing of sections from example casting and test bars as well as impact testing. The impact test temperature will be at room temperature as well as -30C (-20F) as required in GGG 40.3 for example. Ductile to brittle transitions temperature determination could also be determined for select samples. The microstructure of the test bars will be evaluated using quantita- tive metallography. Optical microscopy will be used to determine ferrite grain size. Chemical analysis will also be required. It will be essential to procure castings in this first task that exhibit those properties which both meet as well as exceed the ASTM A536 minimum expectations. The second task will characterize all of the data generated from Task 1 using multiple regression analysis to determine how the different factors interact with the mechanical properties with the intent to isolate those factors that contribute to the high tensile strengths, and yield strengths (and other proper- ties) when the structure is predominantly ferrite. From these results a determination will be made to go to Phase II, which included DOE tests to reproduce these results.


Status Update: The project has begun. Since information on the project is limited at first to the Consortium members and then at a later date to AFS Corporate members, those wishing to participate should contact George Goodrich, Stork CRS, at george.goodrich@us.stork.com.


International Journal of Metalcasting/Winter 10


79


Page 1  |  Page 2  |  Page 3  |  Page 4  |  Page 5  |  Page 6  |  Page 7  |  Page 8  |  Page 9  |  Page 10  |  Page 11  |  Page 12  |  Page 13  |  Page 14  |  Page 15  |  Page 16  |  Page 17  |  Page 18  |  Page 19  |  Page 20  |  Page 21  |  Page 22  |  Page 23  |  Page 24  |  Page 25  |  Page 26  |  Page 27  |  Page 28  |  Page 29  |  Page 30  |  Page 31  |  Page 32  |  Page 33  |  Page 34  |  Page 35  |  Page 36  |  Page 37  |  Page 38  |  Page 39  |  Page 40  |  Page 41  |  Page 42  |  Page 43  |  Page 44  |  Page 45  |  Page 46  |  Page 47  |  Page 48  |  Page 49  |  Page 50  |  Page 51  |  Page 52  |  Page 53  |  Page 54  |  Page 55  |  Page 56  |  Page 57  |  Page 58  |  Page 59  |  Page 60  |  Page 61  |  Page 62  |  Page 63  |  Page 64  |  Page 65  |  Page 66  |  Page 67  |  Page 68  |  Page 69  |  Page 70  |  Page 71  |  Page 72  |  Page 73  |  Page 74  |  Page 75  |  Page 76  |  Page 77  |  Page 78  |  Page 79  |  Page 80  |  Page 81  |  Page 82  |  Page 83  |  Page 84  |  Page 85