Aluminum Base Alloys (chip and disk) (continued)


SRM 1710


1711 1712 1713 1714 1715 2426


Description Alloy 3004


Alloy 3004 Alloy 3004 Alloy 5182 Alloy 5182 Alloy 5182


55% Aluminum Zinc Alloy Unit Size


disk: 63 mm diameter  disk: 63 mm diameter  disk: 63 mm diameter  disk: 63 mm diameter  disk: 63 mm diameter  disk: 63 mm diameter  chip: 31 mm diameter 2 


19 mm 19 mm 19 mm 19 mm 19 mm 19 mm 104


kg - 31 mm diameter


Cobalt Base Alloys (chip and disk) For more information, see Table 102.2 Cobalt Base Alloys (chip and disk) on our website www.nist.gov/srm.


SRM Description


862 High Temperature Alloy L605 1242 High Temperature Alloy L605 1775 Refractory Alloy MP 35 N 2175 Refractory Alloy MP 35 N


Unit Size chip: 100 g


disk: 35 mm diameter  disk: 35 mm diameter  chip: 50 g


19 mm 19 mm


Copper “Benchmark” (chip and rod)


Unit Size: Chip: 50 g Rod: 6.4 min  103 mm For more information, see Table 102.5 Copper Benchmark (chip and rod) on our website www.nist.gov/srm.


SRM


Chip Rod/Chill Cast 494


395 396


398


399 400


498 499 500


C1251a C1252a C1253a


454 (35 g)


495 496 457


Description


Unalloyed Copper - Cu I Unalloyed Copper - Cu II Unalloyed Copper - Cu III Unalloyed Copper - Cu IV Unalloyed Copper - Cu V Unalloyed Copper - Cu V Unalloyed Copper - Cu VI Unalloyed Copper - Cu VII


Phosphorus Deoxidized Copper VIII Phosphorus Deoxidized Copper IX Phosphorus Deoxidized Copper X Unalloyed Copper - Cu XI


WWW.NIST.GOV/SRM  PHONE: (301) 975-2200  FAX: (301) 948-3730  EMAIL: SRMINFO@NIST.GOV


61


INDUSTRIALMATERIALS


Page 1  |  Page 2  |  Page 3  |  Page 4  |  Page 5  |  Page 6  |  Page 7  |  Page 8  |  Page 9  |  Page 10  |  Page 11  |  Page 12  |  Page 13  |  Page 14  |  Page 15  |  Page 16  |  Page 17  |  Page 18  |  Page 19  |  Page 20  |  Page 21  |  Page 22  |  Page 23  |  Page 24  |  Page 25  |  Page 26  |  Page 27  |  Page 28  |  Page 29  |  Page 30  |  Page 31  |  Page 32  |  Page 33  |  Page 34  |  Page 35  |  Page 36  |  Page 37  |  Page 38  |  Page 39  |  Page 40  |  Page 41  |  Page 42  |  Page 43  |  Page 44  |  Page 45  |  Page 46  |  Page 47  |  Page 48  |  Page 49  |  Page 50  |  Page 51  |  Page 52  |  Page 53  |  Page 54  |  Page 55  |  Page 56  |  Page 57  |  Page 58  |  Page 59  |  Page 60  |  Page 61  |  Page 62  |  Page 63  |  Page 64  |  Page 65  |  Page 66  |  Page 67  |  Page 68  |  Page 69  |  Page 70  |  Page 71  |  Page 72  |  Page 73  |  Page 74  |  Page 75  |  Page 76  |  Page 77  |  Page 78  |  Page 79  |  Page 80  |  Page 81  |  Page 82  |  Page 83  |  Page 84  |  Page 85  |  Page 86  |  Page 87  |  Page 88  |  Page 89  |  Page 90  |  Page 91  |  Page 92  |  Page 93  |  Page 94  |  Page 95  |  Page 96  |  Page 97  |  Page 98  |  Page 99  |  Page 100  |  Page 101  |  Page 102  |  Page 103  |  Page 104  |  Page 105  |  Page 106  |  Page 107  |  Page 108  |  Page 109  |  Page 110  |  Page 111  |  Page 112  |  Page 113  |  Page 114  |  Page 115  |  Page 116  |  Page 117  |  Page 118  |  Page 119  |  Page 120  |  Page 121  |  Page 122  |  Page 123  |  Page 124  |  Page 125  |  Page 126  |  Page 127  |  Page 128  |  Page 129  |  Page 130  |  Page 131  |  Page 132  |  Page 133  |  Page 134  |  Page 135  |  Page 136