PRODUCTION • PROCESSING • HANDLING
The EXPANDING UNIVERSE of FLUID FILM BEARING MATERIALS
Sriram Venkatesan outlines differentiating characteristics of fluid film bearing material options, from babbitt to diamond
F
luid film bearings are often designed as a sacrificial component in rotating machines. Te primary characteristics of a bearing material are compatibility, conformability and embeddability. In
broad strokes, compatibility is the resistance to seizure during a metal-to-metal contact event; conformability allows the bearing to conform to minor variations in the counter surface; and embeddability provides the ability to accept small amounts of foreign particles in the lubricant. Tese qualities reduce the likelihood of damage to the shaft during start-up and shutdown, or from upset conditions, misalignments or occasional ingestion of contaminants. A bearing material must also have adequate compressive strength, temperature capability, and corrosion and wear resistance for the given use. To meet the widening range of application
requirements and operating conditions for high- performing rotating equipment, advances in fluid film bearing materials give differing emphasis to these ideal characteristics, sometimes requiring trade-offs. Depending on the particular machine’s needs, fluid film bearing material options include tin-based alloys (babbitt), bronze, aluminium-tin, engineered polymers, ceramics (and cermets) and super-hard materials such as polycrystalline diamond (PCD). Tin-based babbitt, also referred to as whitemetal,
is a ‘soft’ metal that exhibits excellent conformability, compatibility and embeddability. Babbitt has long been a standard for oil-lubricated fluid film bearing materials; however, it is typical industry practice to limit the maximum operating temperature of babbitt bearings to 130°C (266°F). In addition to its low temperature threshold, babbitt has a relatively low fatigue strength compared to advanced materials.
When bearing environment temperatures
increase beyond the limits of babbitt but loads remain relatively low, bronze bearing surfaces can provide additional safety margin at the higher temperature. Successful operational experience of bronze bearings exists at lubricating oil temperatures beyond 150°C (302°F) at relatively low loads.
36
www.engineerlive.com
Te conformability and embeddability of bronze bearings, however, are inferior to those of babbitt.
INCREASED TEMPERATURE AND LOADS Aluminium-tin bearings may provide drop-in replacement for babbitt bearings to increase both temperature and load capability within the same envelope. Aluminium-tin bearings can operate at temperatures up to 160°C (320°F), with a much higher fatigue strength than babbitt. Being a metallic bearing material like babbitt, aluminium-tin allows existing protocols to be used for monitoring bearing health. Aluminium- tin bearings can also increase safety margin in case of an unexpected upset condition such as loss of lubrication or accidental overload. Te embeddability and conformability characteristics of aluminium-tin are superior to bronze. Engineered polymers exhibit embeddability and conformability comparable to babbitt’s, preventing damage to the shaft when small amount of debris enter the lubricant film. Tey have emerged as an effective solution to further expand operating temperature capability and support higher loads. With clean low-viscosity lubricants (such as water), polymer bearing designs have proven to operate reliably on a relatively thin lubricant film.
Tilt-pad journal and combination thrust and journal bearing using engineered polymer
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46 |
Page 47 |
Page 48 |
Page 49 |
Page 50 |
Page 51 |
Page 52