review research A watertight explanation for LED droop?
Experimental measurements of LED droop are replicated with a model that includes carrier leakage
A PARTNERSHIP between Fred Schubert’s team at Rensselaer Polytechnic Institute, New York, and Samsung LED, Korea, claims that it has a new, comprehensive explanation for LED droop. The team’s model for droop, the decline in an LED’s efficiency as its current is cranked up, is based on the leakage of electrons out of the active region of the device.
“[Our] model is able to
conclusively describe all aspects of efficiency droop,” says Schubert. This includes temperature dependence, the dependence on third-order and fourth-order terms of carrier density and the scale of this efficiency-limiting phenomena in different material systems, such as those based on GaN and AlGaInP.
electron and hole mobility and concentration, such as GaN.
When diodes enter the high-level injection regime, some of the applied voltage starts to drop across the low-conductivity p-type layer, and drift current rises with the total current. At high drive currents, it is significant and leads to a reduction in the injection efficiency into the active region. This causes droop in the LED.
Figure 1. Pulsed emission spectra of an InGaN LED reveals the significant difference between lattice and carrier temperatures. Carrier temperatures were extracted from the high energy slope using the an equation: Intensity is proportional to exp(-hυ/kTcarrier
)
Strong asymmetry in electron and hole transport characteristics form the basis for the model, which also includes polarization effects. “The polarization fields lower the effective barrier height of the electron blocking layer, thereby facilitating electron leakage,” explains Schubert.
The origin of LED droop is highly controversial, and several groups have argued that it is predominantly caused by Auger recombination, a process involving three carriers. An Auger-effect contribution that is proportional to the third order of the carrier density is included in the model built by Schubert’s team. Fitting this model to experimental data reveals an Auger coefficient of the order of 10-31
cm6 s-1 , two
orders of magnitude smaller than a drift leakage term, which also depends on the cube of the carrier density.
“Although the Auger effect is real, it is, in the present context, certainly a secondary effect. It’s probably negligible, maybe even irrelevant,” claims Schubert.
Figure 2. At high current densities, the well known ABC model fails to fit experimental results. In comparison, the model of Schubert and co-workers, which include a carrier leakage loss term that depends on the third and fourth order of the carrier density, fits the experimental data very well.
His team’s model, which was built from scratch, accounts for high-injection conditions, where electron drift in the p-type layer leads to a reduction in the injection efficiency. According to the team, droop kicks in when LEDs are operating in the high- level injection regime, which is ‘more easily reached’ when the p-n junction is made from materials that have a strong asymmetry in
Schubert and his co-workers claim that there are three reasons why this leakage current is higher than one might expect: The electron temperature is significantly higher than the lattice temperature (see Figure 1); experimental measurements of tunnelling currents through barriers generally exceed theoretical estimates; and polarization fields can reduce carrier capture and enhance carrier leakage, due to the positive sheet charge at the interface between the electron-blocking-layer and spacer in InGaN LEDs.
An equation that includes third-order and fourth-order terms for drift-induced loss through leakage, plus a third order term for Auger recombination, has been used to fit efficiency- versus-current plots for three high-quality blue LEDs (see Figure 2). The team claims that the theoretical fits to the emission of all three LEDs, which have peak emission between 448 nm and 451 nm, are excellent. They are clearly superior to the widely used ‘ABC’ model, which does not include a fourth-order term.
“Having the understanding and knowledge available for the cause of droop, we will be able to develop the tools that allow us to reduce the droop for blue as well as green emitters,” says Schubert.
G.-B Lin et. al. Appl. Phys. Lett. 100 161106 (2012)
July 2012
www.compoundsemiconductor.net 45
Page 1 |
Page 2 |
Page 3 |
Page 4 |
Page 5 |
Page 6 |
Page 7 |
Page 8 |
Page 9 |
Page 10 |
Page 11 |
Page 12 |
Page 13 |
Page 14 |
Page 15 |
Page 16 |
Page 17 |
Page 18 |
Page 19 |
Page 20 |
Page 21 |
Page 22 |
Page 23 |
Page 24 |
Page 25 |
Page 26 |
Page 27 |
Page 28 |
Page 29 |
Page 30 |
Page 31 |
Page 32 |
Page 33 |
Page 34 |
Page 35 |
Page 36 |
Page 37 |
Page 38 |
Page 39 |
Page 40 |
Page 41 |
Page 42 |
Page 43 |
Page 44 |
Page 45 |
Page 46 |
Page 47 |
Page 48 |
Page 49 |
Page 50 |
Page 51 |
Page 52 |
Page 53 |
Page 54 |
Page 55 |
Page 56 |
Page 57 |
Page 58 |
Page 59 |
Page 60 |
Page 61 |
Page 62 |
Page 63 |
Page 64 |
Page 65 |
Page 66 |
Page 67 |
Page 68 |
Page 69 |
Page 70 |
Page 71 |
Page 72 |
Page 73 |
Page 74 |
Page 75 |
Page 76 |
Page 77 |
Page 78 |
Page 79 |
Page 80 |
Page 81 |
Page 82 |
Page 83 |
Page 84 |
Page 85 |
Page 86 |
Page 87 |
Page 88 |
Page 89 |
Page 90 |
Page 91 |
Page 92 |
Page 93 |
Page 94 |
Page 95 |
Page 96 |
Page 97 |
Page 98 |
Page 99 |
Page 100 |
Page 101 |
Page 102 |
Page 103 |
Page 104 |
Page 105 |
Page 106 |
Page 107 |
Page 108 |
Page 109 |
Page 110 |
Page 111 |
Page 112 |
Page 113 |
Page 114 |
Page 115 |
Page 116 |
Page 117 |
Page 118 |
Page 119 |
Page 120 |
Page 121 |
Page 122 |
Page 123 |
Page 124 |
Page 125 |
Page 126 |
Page 127 |
Page 128 |
Page 129 |
Page 130 |
Page 131 |
Page 132 |
Page 133 |
Page 134 |
Page 135 |
Page 136 |
Page 137 |
Page 138 |
Page 139 |
Page 140 |
Page 141 |
Page 142 |
Page 143 |
Page 144 |
Page 145 |
Page 146 |
Page 147 |
Page 148 |
Page 149 |
Page 150 |
Page 151 |
Page 152 |
Page 153 |
Page 154 |
Page 155 |
Page 156 |
Page 157 |
Page 158 |
Page 159 |
Page 160 |
Page 161 |
Page 162 |
Page 163 |
Page 164 |
Page 165 |
Page 166 |
Page 167 |
Page 168 |
Page 169 |
Page 170 |
Page 171 |
Page 172 |
Page 173 |
Page 174 |
Page 175 |
Page 176 |
Page 177 |
Page 178 |
Page 179 |
Page 180 |
Page 181 |
Page 182 |
Page 183 |
Page 184 |
Page 185 |
Page 186